Advanced-PP 1128N
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Advanced Petrochemical Company |
| Trademark: | Advanced-PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SsGGhZ_Advanced-PP-1128N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced-PP 1128 N is a propylene homopolymer & suited for cast film application. It contains slip & antiblocking agents. Application Cast film & water quenchied tubular film Regulatory Information: The Grade Advanced-PP 1128N and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011. Specific information is available upon request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 76.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 9.0 | % | |
| Break | > 50 | % | |
| Flexural Modulus | DIN 53121 | ||
| Across Flow : 0.0500 mm, Cast Film | 670 | MPa | |
| Flow : 0.0500 mm, Cast Film | 700 | MPa | |
| Coefficient of Friction | 0.18 | DIN 53375 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Elongation | DIN 53455 | ||
| MD : Break, 50 µm, Cast Film | 680 | % | |
| TD : Break, 50 µm, Cast Film | 720 | % | |
| Dart Drop Impact 1(50 µm, Cast Film) | 280 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm, Cast Film) | 100 | ISO 2813 | |
| Haze (1000 µm, Injection Molded) | 2.7 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | DIN 53455 | ||
| MD : 50.0 µm | 42.0 | MPa | |
| TD : 50.0 µm | 38.0 | MPa |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FE-361U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| DynaMix™ 2044-GBID | Polymer Dynamix | Nylon, Unspecified | DynaMix™ |
| PELPRENE™ P150B | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| Sylvin 7843-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ WF006H compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |