TOTAL Polystyrene Crystal 1160
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SsENRx_TOTAL-Polystyrene-Crystal-1160.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYSTYRENE CRYSTAL 1160 is a high heat resistance, high molecular weight crystal polystyrene mainly for the extrusion industry. Most notably for the production of bi-oriented polystyrene (BOPS). It is particularly useful in the production of sheet for food packaging and insulation board made by direct gassing, where it gives expanded sheets with high mechanical properties. POLYSTYRENE CRYSTAL 1160 can be used pure for the production of transparent cups or in dilution with POLYSTYRENE IMPACT 7240 for the extrusion of sheet for hot-fill thermoforming applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.4 | g/10 min | ISO 1133 |
| Melt volume-flow rate (200°C/5.0 kg) | 2.50 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | < 0.10 | % | ISO 62 |
| Saturation | 0.10 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 3200 | MPa | ISO 527-2 |
| -- | 3000 | MPa | ISO 527-2 4 |
| Tensile Stress | |||
| Break | 48.0 | MPa | ISO 527-2 |
| Break | 50.0 | MPa | ISO 527-2 5 |
| Tensile Strain | |||
| Break | 3.0 | % | ISO 527-2 |
| Break | 2.0 | % | ISO 527-2 6 |
| Tensile Creep Modulus (1 hr) | 3150 | MPa | ISO 899-1 7 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | |||
| -- | 8.0 | kJ/m² | ISO 179/1eU |
| 23°C | 16.0 | kJ/m² | ISO 179/1eU 8 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 97.0 | °C | ISO 75-2/A |
| 1.8 MPa | 97.0 | °C | ISO 75-2 9 |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/A50 |
| -- | 101 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 98.0 | °C | ISO 306 10 |
| CLTE | |||
| Flow | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse | 7.0E-5 | cm/cm/°C | ISO 11359-2 11 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | > 1.0E+15 | ohms | IEC 60093 |
| -- | 1.0E+14 | ohms | IEC 60093 12 |
| Electric Strength | 140 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | ISO 1210 13 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 TFE 10 | RTP Company | Nylon 66 | RTP |
| Sylvin 8301-90LG Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polypropylene PPH 4060 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Elastron® V V101.A55.B | Elastron USA, Inc. | TPV | Elastron® V |
| Petro Rabigh PP FS2011E | Rabigh Refining & Petrochemical Co. | PP Homopolymer | Petro Rabigh PP |