AFFINITY™ SQ 1503UE
| Category: | POP , Polyolefin Plastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | AFFINITY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SsAK1y_AFFINITY-SQ-1503UE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AFFINITY™ SQ 1503 UE Polyolefin Plastomer is a Polyolefin Plastomer (POP) produced using INSITE™ Technology. AFFINITY SQ 1503 UE Polyolefin Plastomer is specifically designed for rotomoulding applications. It offers easy demoulding combined with flexibility and elastic recovery normally associated with polar copolymers such as EBA, EVA and plasticised PVC. Processing and Stabilisation: The inherently stable POP is further stabilised against heat and UV-radiation. The result is a wide processing latitude, good colour retention and long life expectancy. Availability: AFFINITY SQ 1503 UE Polyolefin Plastomer is available as free flowing powder ground to 500 micron. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Antarox, Compression Molded | > 1000 | hr | |
| 50°C, 100% Antarox, Compression Molded | > 1000 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Compression Molded | 92 | ||
| Shore D, Compression Molded | 40 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 5.00 | MPa | |
| Yield, Rotational Molded | 5.00 | MPa | |
| Break, Compression Molded | 21.0 | MPa | |
| Break, Rotational Molded | 19.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Break, Compression Molded | 1200 | % | |
| Break, Rotational Molded | 1000 | % | |
| Flexural Modulus - 2% Secant | ASTM D790 | ||
| Compression Molded | 81.0 | MPa | |
| Rotational Molded | 70.0 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set 1(100% Strain) | 10 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Falling Dart Impact | ISO 6603-2 | ||
| -20°C 2 | > 150 | J/cm | |
| -20°C 3 | > 150 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 82.0 | °C | ISO 306/120 |
| Melting Temperature | 97.0 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 80.0 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Rotational Molded |
| 2 . | Rotational Molded, No break |
| 3 . | Compression Molded, No break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 3320EH | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SEPAZ™ K115HF | Mando Advanced Materials Co., Ltd. | PPS | SEPAZ™ |
| DESLOY™ DSC891A | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| Huafon T26P | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| TechnoFin PP GF 20 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |