KOPA® KN133G10
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SrgvRN_KOPA-KN133G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPA® KN133G10 is a Polyamide 6 (Nylon 6) product filled with glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 0.90 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 102 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4450 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 125 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648A | ||
| 0.45 MPa, Unannealed | 205 | °C | |
| 1.8 MPa, Unannealed | 185 | °C | |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.60 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michiloy MT11220 | API Polymers, Inc. | PC+PBT | Michiloy |
| TEKAPPO™ J100 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| Torayca® NX85T-10A | Toray Resin Company | PC | Torayca® |
| TUFNYL® SXXIC BLUE | SRF Ltd. | Nylon 6 | TUFNYL® |
| Hylon® N2213STHL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |