CP PRYME® ABS A100-88
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SnVVTv_CPPRYMEABSA10088.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime ABS, General Purpose, Natural |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 5.6 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2140 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 40.7 | MPa | ASTM D638 |
| Fracture | 31.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.0 | % | ASTM D638 |
| Fracture, 23°C | 20 | % | ASTM D638 |
| Flexural Modulus (50.0 mm Span) | 2210 | MPa | ASTM D790 |
| Flexural Strength (Yield, 50.0 mm Span) | 68.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 320 | J/m | ASTM D256 |
| Instrumented Dart Impact | 30.3 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 96.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 82.2 | °C | ASTM D648 |
| Vicat Softening Temperature | 98.9 | °C | ASTM D1525 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.8E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 - 93 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 188 - 210 | °C | |
| Middle Temperature | 204 - 227 | °C | |
| Front Temperature | 216 - 238 | °C | |
| Nozzle Temperature | 218 - 260 | °C | |
| Mold Temperature | 49 - 71 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 167 NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| SUPREME HIPS SH 3001 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Argyle ABS (P400) | Argyle Materials Inc. | ABS | Argyle |
| Gallonprene® GP310-6502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hifax TYC 007P E C13101 | LyondellBasell Industries | PP Copolymer | Hifax |