LNP™ COLORCOMP™ J1000E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SnOvDS_LNP-COLORCOMP-J1000E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP COLORCOMP J1000E is a compound based on PES resin. Added features include: Easy Moulding. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.90 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 91.0 | MPa | |
| Break | 65.0 | MPa | |
| Tensile Strain (Yield) | 6.8 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2800 | MPa | ISO 178 |
| Flexural Stress | 136 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 197 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 ST VRM0076 NR325 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Forprene® 6NM001A55 | SO.F.TER. SPA | TPV | Forprene® |
| MAJORIS DW434E/8 | AD majoris | HDPE | MAJORIS |
| Sylvin 8225-75 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dow Corning® QP1-260 | Dow Corning Corporation | Silicone | Dow Corning® |