SLOVAMID® 66 GF 40 E/3M
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SmDSQT_SLOVAMID-66-GF-40-E-3M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66 for extrusion and injection moulding grade. Chemically reinforced with 40% glass fibre, determined for extrusion of profile systems for window profiles. Delivered in black color. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 195 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8700 | MPa | ISO 178 |
| Flexural Stress | 250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 60 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 255 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 250 | °C | ISO 306/B |
| Melting Temperature (DSC) | 260 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 37W300 | AD majoris | PBT | MALAT |
| RTP 285 HEC | RTP Company | Nylon 66 | RTP |
| POYAD CR102 | Pooya Polymer Tehran | PP Homopolymer | POYAD |
| Chemical Resources GPPS0600REP | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| Hostaform® C 13021 RM | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |