PENTAMID B L5 R H schwarz
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sm2mHg_PENTAMID-B-L5-R-H-schwarz.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, impact modified, heat stabilised polyamide 6 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction | 2.0 | -- | % | ISO 294-4 |
| Flow direction | 1.8 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.8 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 120 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2450 | 1050 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 65.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | 15 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 222 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength (1.00 mm) | 32 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | -- | IEC 60250 | |
| Comparative Tracking Index | 575 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 ISO Description: PA6-HI, MHRC, 14-020The value listed as Melting Point, ISO 3146, was tested in accordance with ISO 11357. |
| 调节后的 ISO Description: PA6-HI, MHRC, 14-020 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.14 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 250 - 275 | °C | |
| Middle Temperature | 265 - 280 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Processing (Melt) Temp | 270 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 55.0 | MPa | |
| Holding Pressure | 33.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 HF | RTP Company | PEEK | RTP |
| RheTech Thermoplastic Polyolefin FT7012-707UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| SNOLEN® EP 0.26/51 N | JSC Gazprom neftekhim Salavat | HDPE | SNOLEN® |
| TAIRILOY AC3250 | Formosa Plastics Corporation | PC+ABS | TAIRILOY |
| Polychim HA10XT | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |