ADPOLY TU-100
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | ADPOLY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sl66Xu_ADPOLY-TU-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TU-100 is LDPE based adhesive resin containing anhydride. This grade shows a strong adhesion to PE, PA, EVOH, and it has polyolefin-like properties. In addition, its processability is excellent. TU-100 is mainly intended for use as an adhesive resin in multi-layer bottle. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.4 to 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 38 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 9.12 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 108 | MPa | ASTM D790 |
| Flexural Strength | 4.71 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 570 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 78.0 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion Strength | > 3.00 | kgf/2 cm | ASTM D903 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SD101G10 | RJM International, Inc. | PC | RJM |
| NuSil R-2615-3 | NuSil Technology | Silicone | NuSil |
| ALCUDIA® EVA PA-440 | REPSOL | EVA | ALCUDIA® EVA |
| Edgetek™ EM01042076BG | PolyOne Corporation | PC | Edgetek™ |
| Lupoy® GP2200 | LG Chem Ltd. | PC | Lupoy® |