TECHNYL® PSB 286 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SkgKxq_TECHNYL-PSB-286-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced polyamide PA6, with very good lubrication, standard for fast injection cycles, for injection moulding. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.6 | -- | % | |
| Flow | 1.2 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3000 | 1300 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 80.0 | 41.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 85 | 45 | % | |
| Break | 65 | 82 | % | |
| Flexural Modulus | 2800 | 1000 | MPa | ISO 178 |
| Flexural Stress | 115 | 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | 81 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.40 | 3.90 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-2 | -- | ||
| 1.60 mm | V-2 | -- | ||
| 3.20 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 700 | -- | °C | |
| 1.60 mm | 700 | -- | °C | |
| 3.20 mm | 750 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 225 to 230 | °C | |
| Middle Temperature | 230 to 235 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Mold Temperature | 20.0 to 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9712-90UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| FireCon™ CPE 30-11 RoHS BLACK | PolyOne Corporation | CPE | FireCon™ |
| Jackdaw PP ES10NT6472 | Jackdaw Polymers | PP, Unspecified | Jackdaw PP |
| LNP™ THERMOTUF™ VF004S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |
| Hifax TYC 900P C11370 | LyondellBasell Industries | PP, Unspecified | Hifax |