Boltaron 4332

Category:	PMMA+PVC , Acrylic (PMMA) + PVC
Manufacturer:	Boltaron Performance Products
Trademark:	Boltaron
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SkRWrn_Boltaron-4332.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Impact resistance of 20 ft lbs/in (1060 J/m) and other outstanding properties make Boltaron 4332 the ultimate Acrylic/PVC alloy for your most demanding applications Boltaron 4332 sheet is a proprietary, fire retardant, PVC/Acrylic alloy that offers outstanding physical properties, making it the ideal material from which to thermoform and fabricate parts subjected to high impact, abrasion, harsh chemicals and/or temperature extremes. With an Izod impact rating of 20 ft lbs/in (1060 J/m) Boltaron 4332 is among the most impact resistant PVC/Acrylic alloys ever produced. It is also exhibits extreme resistance to heat deformation and cold weather cracking, and is highly resistant to caustic and acidic chemicals spanning the entire pH range, in addition to offering greater abrasion resistance than stainless steel. At the same time, Boltaron 4332 is non-hygroscopic, eliminating the time and cost associated with pre-drying other thermoplastics, and is readily thermoformed, yielding uniform wall thickness in deep recesses and on sharp outside corners. It is also readily sawn, drilled, tapped, routed and otherwise machined using conventional tools, and can be brake formed (thinner gauges), heat welded, adhesive bonded and mechanically fastened, allowing rapid fabrication of a broad range of high-integrity parts and assemblies. Easy to use but difficult to damage, Boltaron 4332 eliminates the compromise associated with lesser PVC/acrylic alloys, FR ABS, and other fire rated thermoplastics, meeting and exceeding the most demanding requirements of fomers, fabricators and OEMs alike.

Message

Impact resistance of 20 ft lbs/in (1060 J/m) and other outstanding properties make

Boltaron 4332 the ultimate Acrylic/PVC alloy for your most demanding applications Boltaron 4332 sheet is a proprietary, fire retardant, PVC/Acrylic alloy that offers outstanding physical properties, making it the ideal material from which to thermoform and fabricate parts subjected to high impact, abrasion, harsh chemicals and/or temperature extremes.

With an Izod impact rating of 20 ft lbs/in (1060 J/m) Boltaron 4332 is among the most impact resistant PVC/Acrylic alloys ever produced.

It is also exhibits extreme resistance to heat deformation and cold weather cracking, and is highly resistant to caustic and acidic chemicals spanning the entire pH range, in addition to offering greater abrasion resistance than stainless steel.

At the same time, Boltaron 4332 is non-hygroscopic, eliminating the time and cost associated with pre-drying other thermoplastics, and is readily thermoformed, yielding uniform wall thickness in deep recesses and on sharp outside corners.

It is also readily sawn, drilled, tapped, routed and otherwise machined using conventional tools, and can be brake formed (thinner gauges), heat welded, adhesive bonded and mechanically fastened, allowing rapid fabrication of a broad range of high-integrity parts and assemblies.

Easy to use but difficult to damage, Boltaron 4332 eliminates the compromise associated with lesser PVC/acrylic alloys, FR ABS, and other fire rated thermoplastics, meeting and exceeding the most demanding requirements of fomers, fabricators and OEMs alike.

General Information
Additive	Flame Retardant
Features	Flame Retardant Good Abrasion Resistance Good Chemical Resistance Good Crack Resistance High Impact Resistance
Uses	Housings
Agency Ratings	FAR 25.853
UL File Number	E54688
Appearance	Colors Available
Forms	Sheet
Processing Method	Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.35	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	106		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	39.3	MPa	ASTM D638
Flexural Modulus	2120	MPa	ASTM D790
Flexural Strength (Yield)	60.0	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	1100	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed)	75.3	°C	ASTM D648

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.02 mm	V-0 5VB
3.18 mm	V-0 5VA
FAA Flammability ¹			FAR 25.853
1.02 mm	12.0	sec
3.18 mm	60.0	sec

Additional Information	Nominal Value	Unit
Forming Temperature	168 to 196	°C

Note Message
1 .	Pass

Resin Grade	Manufacturer	Category	Trademark
Rotec® ABS 1001 F	ROMIRA GmbH	ABS	Rotec® ABS
Grilamid® XE 4180 nat	EMS-GRIVORY	Nylon 1010	Grilamid®
ISOTHANE® 1090A	Great Eastern Resins Industrial Co Ltd (GRECO)	TPU-Polyester	ISOTHANE®
MAJORIS GN040X	AD majoris	PP Homopolymer	MAJORIS
Lusin® Lub PZO 152	Chem-Trend L.P.	Unspecified	Lusin®