Polifil® PP RP-PP Copolymer
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SiVKgN_Polifil-PP-RP-PP-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® Nylon 6/6 combines good abrasion and chemical resistance. These properties have been proven to work in the following applications: valves, bearings, and bearing cages. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D1415 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1380 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 11 | % | |
| Break, 23°C | 50 | % | |
| Flexural Modulus - Tangent (23°C) | 1240 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 2.71 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 93.3 | °C | |
| 1.8 MPa, Unannealed | 48.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6000 B68 | Spartech Polycom | PP, Unspecified | Spartech |
| Complet® LCF50-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| Karina BEIGE PVC COMPOUND 828-08/20-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina MBU GREEN -E 40/587-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 5143-88 Blue 8256 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |