ExxonMobil™ LDPE EVA Copolymers LD 364HE
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | ExxonMobil™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ShEGxC_ExxonMobil-LDPE-EVA-Copolymers-LD-364HE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LD 364HE is an LDPE, offering a good combination of mechanical, optical and sealing properties. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 5.0 | wt% | ExxonMobil Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 170 | MPa | ASTM D882 |
| 1% secant, TD | 200 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 26.0 | MPa | ASTM D882 |
| TD : Fracture | 24.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 170 | % | ASTM D882 |
| TD : Fracture | 540 | % | ASTM D882 |
| Dart Drop Impact | 360 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 180 | g | ASTM D1922 |
| TD | 110 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 52 | ASTM D2457 | |
| Haze | 9.8 | % | ASTM D1003 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRENE® 5890F | SK Global Chemical | EPDM | SUPRENE® |
| UMG ALLOY® CV202 | UMG ABS, Ltd. | PC+ABS | UMG ALLOY® |
| ARLEN™ CH230N | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |
| LNP™ STAT-KON™ DD000 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Hostacom HKC 431N D72643 | LyondellBasell Industries | PP Homopolymer | Hostacom |