EcoPaXX® Q-HGM24
| Category: | Nylon 410 , Polyamide 410 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | EcoPaXX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SghTgi_EcoPaXX-Q-HGM24.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EcoPaXX® Q-HGM24 is a Polyamide 410 (Nylon 410) material filled with 10% glass fiber and 20% mineral. It is available in Asia Pacific, Europe, or North America. Important attributes of EcoPaXX® Q-HGM24 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.65 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8000 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 95.0 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.6 | % | ISO 527-2 |
| Flexural Modulus | 6650 | 4400 | MPa | ISO 178 |
| Flexural Stress | 175 | 115 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 4.0 | 5.3 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 35 | 40 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 235 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 250 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 4.8E-5 | -- | cm/cm/°C | |
| Transverse | 7.5E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Biobased Content - Carbon | 70 | -- | % | ASTM D6866 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 300 | °C | |
| Processing (Melt) Temp | 275 to 310 | °C | |
| Mold Temperature | 80.0 to 140 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 660.6 | RTP Company | ABS | RTP |
| Radilon® A RV250LW 100 NAT 4861 | Radici Plastics | Nylon 66 | Radilon® |
| Ferro PP NPP00GW22GY | Ferro Corporation | PP, Unspecified | Ferro PP |
| Globalene® ST611 | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| Karina CLEAR PVC COMPOUND 40/205 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |