Edgetek™ 5209 Black 30 A 1
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sg9ZMz_Edgetek-5209-Black-30-A-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1(190°C/2.16 kg) | 8.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.5 to 2.7 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2520 | MPa | ASTM D638 |
| Tensile Strength 3(Yield) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2520 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 69 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 110 | °C | ASTM D648 |
| CLTE - Flow | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 188 to 210 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8233G HS | BASF Corporation | Nylon 6 | Ultramid® |
| Borealis PP QB370 | Borealis AG | PP, Unspecified | Borealis PP |
| Arnite® A04 900 | DSM Engineering Plastics | PET | Arnite® |
| Karina BLACK PVC COMPOUND 807D48/ 1-C-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina GREEN PVC COMPOUND 650-40/57 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |