Borealis PP BHC5012C
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SfLAIu_Borealis-PP-BHC5012C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BHC5012C is a polypropylene copolymer intended for injection moulding, extrusion and blow moulding. This material has excellent balanced mechanical properties and is easy to process. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.9 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1150 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 27.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, Injection Molded) | 11 | % | ISO 527-2/50 |
| Flexural Modulus 1(Injection Molded) | 1350 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, injection molding | 3.8 | kJ/m² | ISO 179/1eA |
| -20°C, injection molding | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 75 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | No Break | ISO 179/1eU | |
| 23°C, injection molding | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 5.5 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 55 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 65.0 | °C | ISO 306/B50 |
| Melt Energy | 86.8 | kJ/kg | ISO 11357 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission - 30 | µgC/g | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back pressure: Low to mediumScrew speed: Low to mediumFlow front speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F800E (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| Fortron® 4184L6 | Celanese Corporation | PPS | Fortron® |
| Hanwha Total PP RP100 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Kaneka MUH LG5012 | Kaneka Corporation | ABS | Kaneka MUH |
| Optix® CA-927 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |