Karina WHITE PVC COMPOUND -E 830-10/145-A-ERYB-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SfKy9N_Karina-WHITE-PVC-COMPOUND--E-830-10-145-A-ERYB-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND RECOMMENDED FOR EXTRUSION OF PROFILES FOR GENERAL APPLICATIONS. IT IS SUPPLIED IN PELLET FORM AND SHOULD BE PROCESSED AT THE TEMPERATURE RANGE OF 170C TO 190C. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.42 to 1.48 | g/cm³ | ASTM D792 |
| Color a | -1.61 to -0.0100 | ME 12 | |
| Color b | -1.39 to 0.210 | ME 12 | |
| Color L | 91.4 to 93.0 | ME 12 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | > 76 | °C | ASTM D648 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 78 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | > 3290 | MPa | ASTM D638 |
| Tensile Strength | > 39.3 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 38 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | > 80.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-747 | CHI MEI CORPORATION | ABS | POLYLAC® |
| RTP 2740 S-80A | RTP Company | SEBS | RTP |
| SCHULADUR® A3 GF30 | A. Schulman Inc. | PBT+ASA | SCHULADUR® |
| Formolene® 2610A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| INVISION™ GX 5080G2N | A. Schulman Inc. | TPE | INVISION™ |