Sarlink® TPV 3135
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SfBiWg_Sarlink-TPV-3135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A low hardness, multi-purpose thermoplastic elastomer featuring excellent compression set and high temperature performance. Sarlink® 3135 can be processed by injection molding or extrusion for applications such as grips, seals, gaskets, profiles and other articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792, ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 38 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 43 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : 100% strain | 1.10 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 2.10 | MPa | ASTM D412, ISO 37 |
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 4.00 | MPa | ASTM D412, ISO 37 |
| Flow : Fracture | 2.20 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation | |||
| Transverse flow : Fracture | 600 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 200 | % | ISO 37, ASTM D412 |
| Tear Strength - Across Flow | |||
| -- | 15 | kN/m | ASTM D624 |
| -- 1 | 15 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 15 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 30 | % | ASTM D395, ISO 815 |
| 125°C, 70 hr | 52 | % | ASTM D395, ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | 0.0 | % | ASTM D573, ISO 188 |
| 100% strain 135°C, 1000 hr | 4.0 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | 4.0 | % | ASTM D573, ISO 188 |
| 100% strain 150°C, 168 hr | 11 | % | ASTM D573, ISO 188 |
| Changes in tensile stress upon fracture in air- Transverse flow | |||
| 135°C, 1000 hr | -2.0 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | 1.0 | % | ISO 188, ASTM D573 |
| Change in Shore Hardness in Air | |||
| Support a, 135°C, 1000 hr | -1.0 | ASTM D573, ISO 188 | |
| Support a, 150°C, 168 hr | 1.0 | ISO 188, ASTM D573 | |
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 150 | % | ASTM D471, ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, All Colors) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 270 | Pa·s | ASTM D3835 |
| 200°C | 270 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 182 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 0.345 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 204 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 188 - 210 | °C | |
| Melt Temperature | 193 - 216 | °C | |
| Die Temperature | 193 - 216 | °C | |
| Take-Off Roll | 21.1 - 48.9 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 MeshScrew: General PurposeCompression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGV HZ 15 Natural | Radici Plastics | Nylon 6 | Radilon® |
| Xuchuan XCS-2086B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Elastane™ 4721R10 | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Generic SBC | Generic | SBC | Generic |
| LUVOCOM® 1100-8166 | Lehmann & Voss & Co. | PESU | LUVOCOM® |