NORYL™ FE1410PW resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Semw2Q_NORYL-FE1410PW-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL FE1410PW resin is a blend of polyphenylene Oxide (PPO) and polystyrene (PS) resin that contains 10% glass reinforcement. The resin is suitable for injection molding. NORYL FE1410PW resin has been developed for fluid engineering applications that require improved hydrolytic stability. NORYL FE1410PW resin has been certified for potable water applications up to 85C in Europe and North America in limited colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 32.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | Internal Method |
| Water Absorption | |||
| Saturation, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 50% RH | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4780 | MPa | ASTM D638 |
| -- | 4930 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 94.0 | MPa | ASTM D638 |
| Break | 94.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.8 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 4860 | MPa | ASTM D790 |
| -- 5 | 4880 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 135 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength 7 | ISO 179/1eU | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 35 | J/m | ASTM D256 |
| -30°C 8 | 4.0 | kJ/m² | ISO 180/1A |
| 23°C 9 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 230 | J/m | ASTM D4812 |
| 23°C | 230 | J/m | ASTM D4812 |
| -30°C 10 | 13 | kJ/m² | ISO 180/1U |
| 23°C 11 | 13 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 100 mm Span 12 | 135 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 3.20 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 126 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 146 | °C | ISO 306/A50 |
| -- | 140 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellidor B 631-10S | ALBIS PLASTIC GmbH | CAB | Cellidor |
| Elastron® V V201.D40.B | Elastron USA, Inc. | TPV | Elastron® V |
| Hyundai EP PPF HG960 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| LIHAN® A100 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| Sarlink® TPE ML-1140N NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |