Ecomann® Bioresin EM20030
| Category: | PHA , Polyhydroxyalkanoate |
| Manufacturer: | Shenzhen Ecomann Biotechnology Co., Ltd. |
| Trademark: | Ecomann® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SeXwVP_Ecomann-Bioresin-EM20030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EM20030 is semi-crystalline biodegradable, aliphatic bio-polyester designed for use in injection molding applications.EM20030 is PHA base compound with PLA, plant fibers and some additives... EM20030 is certificated to meet EN13432 & ASTM D6400 standards for biodegradable plastics Typical applications: Paint brush handles and wood color injection molding products |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (170°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Water Absorption (Equilibrium) | < 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (Area) | 3.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| Melting Temperature | 140 to 160 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 135 to 145 | °C | |
| Middle Temperature | 145 to 150 | °C | |
| Front Temperature | 150 to 155 | °C | |
| Nozzle Temperature | 150 to 155 | °C | |
| Mold Temperature | 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 PA-121G33 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Geon™ Vinyl Fittings M1030 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Fittings |
| KPOL-PP K-PPH 5.0 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Iupilon® GSH2020DR 9913A | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Ultramid® Structure A3WG12 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |