Karina PVC COMPOUND - IVORY E-105900-35/ 1-B-AC-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SeMFCG_Karina-PVC-COMPOUND---IVORY-E-105900-35-1-B-AC-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PVC COMPOUND 105 C ( ANTI-FLAME AND HEAVY METAL FREE ) RECOMMENDED FOR ISOLATION AND COVERING ELECTRICAL WIRES FOR INTERNAL ELECTRICAL EQUIPAMENTS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.35 - 1.41 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | ppm | ASTM D1971 | |
| Chromium Content | ppm | ASTM D1971 | |
| Color a | -1.83 - 1.17 | ME 12 | |
| Color b | 3.99 - 6.99 | ME 12 | |
| Color L | 89.3 - 92.3 | ME 12 | |
| Mercury Content | ppm | ASTM D1971 | |
| Color | OK | ME 12 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | ppm | IEC 62321 | |
| Maximum Variation of Elongation | % | IEC 60811-1-2 | |
| Maximum Variation of Tensile Strength | % | IEC 60811-1-2 | |
| Lead content | ppm | ASTM D1971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 88 - 92 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 12.6 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 150 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | NBR 5403 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 30 | % | NBR 6245 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aging Air 168 hr at 136°C |
| 3 . | Aging air 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0230 | Borealis AG | Plastomer | Queo™ |
| NatureFlex™ 80NP | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Nypel® RC6024 BK | BASF Corporation | Nylon 6 | Nypel® |
| LEXAN™ MLS43R resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| TOTAL Polystyrene Impact 4440H | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |