Petrotene® PP A3 T10 AML PH314
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SeB6cW_Petrotene-PP-A3-T10-AML-PH314.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene with 10% mineral filler for injection molding, resistant to oil, grease and many solvents, good set of mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.00 to 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 to 1.5 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNOGRAN® PA66 50%FV BLK | Eurocompound Polymers | Nylon 66 | TECHNOGRAN® |
| MOSTEN MA 712 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| VESTOLIT® P 1382 K | VESTOLIT GmbH & Co. KG | PVC, Unspecified | VESTOLIT® |
| TERRAMAC TE-1030 | UNITIKA Plastics Division | PLA | TERRAMAC |
| POCAN® B 2505 000000 | LANXESS GmbH | PBT | POCAN® |