Order Products : sales@su-jiao.com
UNITIKA Nylon 66 A175G15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | UNITIKA Nylon 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Scrood_UNITIKA-Nylon-66-A175G15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNITIKA Nylon 66 A175G15 is a Polyamide 66 (Nylon 66) material filled with 15% glass fiber. It is available in Asia Pacific or North America. Primary attribute of UNITIKA Nylon 66 A175G15: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.26 | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 3.20 mm | 1.5 | 1.5 | % | |
| Flow : 3.20 mm | 0.60 | 0.60 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | 1.9 | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5700 | 3500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 73.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 5000 | 3200 | MPa | ISO 178 |
| Flexural Stress | 188 | 110 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 30 | 39 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 252 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 229 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 4.2E-5 | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 33 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.40 | -- | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.840 mm) | HB | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M864E | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| SCHULAKETON GF 15 | A. Schulman Europe | PK-Aliphatic | SCHULAKETON |
| Witcom PA66 3C | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| DuraElast 910 | Evermore Chemical Industry Co., Ltd. | TPU, Unspecified | DuraElast |
| KOPA® KN133G45 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |