Aristech Acrysteel® M
| Category: | Acrylic, Unspecified , Acrylic |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sc3zPS_Aristech-Acrysteel-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Acrysteel® M is a continuous cast partially cross-linked impact acrylic sheet designed specifically for marine applications. The following physical properties were determined using 0.150" (3.81 mm) thickness Aristech Acrylics LLC Acrysteel® M acrylic sheet. Properties may vary somewhat for other thicknesses and/or between opaque colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D4802 | ||
| Flow : 3.81 mm | 2.2 | % | |
| Across Flow : 3.81 mm | 1.9 | % | |
| Water Absorption (Saturation, 3.81 mm) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 3.81 mm) | 88 | ASTM D785 | |
| Barcol Hardness (3.81 mm) | 40 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.81 mm) | 2870 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.81 mm) | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.81 mm) | 14 | % | ASTM D638 |
| Flexural Modulus (3.81 mm) | 2730 | MPa | ASTM D790 |
| Flexural Strength (3.81 mm) | 94.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (3.81 mm) | 544 | J/m | ASTM D6110 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Stability 2(180°C, 3.81 mm) | No Effect | ASTM D4802 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Forming Temperature (3.81 mm) | 160 to 182 | °C | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.81 mm) | 59 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.81 mm) | 80.0 | °C | ASTM D648 |
| CLTE - Flow (3.81 mm) | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | 0.150 in |
| 2 . | 30 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDINYL C2 M20 V10 | ADDIPLAST | Nylon 66/6 | ADDINYL |
| Elastron® D D401.A60.N | Elastron USA, Inc. | SBS | Elastron® D |
| Hybrid B2026G30 | Ravago Manufacturing Americas, LLC | PC+PBT | Hybrid |
| LNP™ THERMOCOMP™ LF006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |
| Lupolen 2420 F PLUS | LyondellBasell Industries | LDPE | Lupolen |