ULTEM™ AUT230 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Sc16Uh_ULTEM-AUT230-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent polyetherimide (Tg 247 degC). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 230 degC (SABIC Innovative Plastics method) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.70 | % | |
| Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.70 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.8 | % | |
| Equilibrium, 23°C, 50% RH | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3510 | MPa | ASTM D638 |
| -- | 3110 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 96.0 | MPa | ASTM D638 |
| Yield | 95.0 | MPa | ISO 527-2/5 |
| Break 4 | 96.0 | MPa | ASTM D638 |
| Break | 78.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 6.0 | % | ASTM D638 |
| Yield | 8.5 | % | ISO 527-2/5 |
| Break 6 | 25 | % | ASTM D638 |
| Break | 17 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 7 | 3170 | MPa | ASTM D790 |
| -- 8 | 3080 | MPa | ISO 178 |
| Flexural Stress | 123 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -30°C | 74 | J/m | ASTM D256 |
| 23°C | 69 | J/m | ASTM D256 |
| -30°C 9 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 10 | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 11 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 33.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 237 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 217 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 230 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 228 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 242 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 238 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 150°C | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 230 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Nozzle Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 349 to 399 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 815C | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| VITAMIDE® BS10VN6313 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Akulon® Ultraflow K-FG0 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| FRblend® PBT-1307 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| ESTADIENE 1218 HT V0 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |