CYCOLAC™ MG38U resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SbPXAW_CYCOLAC-MG38U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact ABS. UL 746C f1 listed. Toughness/rigidity. Good fatigue resistance. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2390 | MPa | ASTM D638 |
| -- | 2420 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.8 | MPa | ASTM D638 |
| Yield | 41.0 | MPa | ISO 527-2/5 |
| Break 3 | 36.2 | MPa | ASTM D638 |
| Break | 33.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 2.5 | % | ISO 527-2/5 |
| Break 5 | 98 | % | ASTM D638 |
| Break | 30 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2410 | MPa | ASTM D790 |
| -- 7 | 2310 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 76.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D256 |
| 23°C 9 | 27 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 32.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 80.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525, ISO 306/B50 10 11 |
| -- | 99.0 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.6E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 to 70 | % | |
| Rear Temperature | 188 to 210 | °C | |
| Middle Temperature | 204 to 227 | °C | |
| Front Temperature | 216 to 238 | °C | |
| Nozzle Temperature | 218 to 260 | °C | |
| Processing (Melt) Temp | 218 to 260 | °C | |
| Mold Temperature | 48.9 to 71.1 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7530 GK 10 GF 20 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Andur AL 62 DP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| apilon 52c® ESC 62 | API SpA | TPU-PC | apilon 52c® |
| Sylvin 4200-88UV Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Zytel® 73G40T BK416 | DuPont Performance Polymers | Nylon 6 | Zytel® |