PULSE™ 2100LG
| Category: | PC+ABS , PC/ABS Engineering Resin |
| Manufacturer: | Trinseo |
| Trademark: | PULSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SbH134_PULSE-2100LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PULSE™ 2100LG Engineering Resin is designed to provide top performance in tough applications, from single piece items to intricate components. Ideal for energy management solutions, it can withstand high and low temperature extremes and rapid, repeated temperature fluctuations. Benefits:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792, ISO 1183/B |
| -- | 1130 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 4.5 | g/10 min | ASTM D1238 |
| 260°C/3.8 kg | 4.5 | g/10 min | ISO 1133 |
| Melt volume-flow rate (230°C/3.8 kg) | 1.00 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage | |||
| Flow | 0.60 | % | ASTM D955 |
| -- | 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 3.20 mm, Injection Molded | 2340 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2 |
| -- | 2090 | MPa | ISO 527-2 3 |
| Tensile Strength | |||
| Yield, 3.20 mm, Injection Molded | 53.1 | MPa | ASTM D638 |
| Yield | 51.0 | MPa | ISO 527-2 |
| Yield | 48.0 | MPa | ISO 527-2 4 |
| Break, 3.20 mm, Injection Molded | 53.8 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 3.20 mm, Injection Molded | 5.0 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2 |
| Yield | 4.9 | % | ISO 527-2 5 |
| Break, 3.20 mm, Injection Molded | 130 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2 |
| Nominal strain at break | > 50 | % | ISO 527-2 6 |
| Flexural Modulus | |||
| 3.20 mm, Injection Molded | 2340 | MPa | ASTM D790 |
| -- | 2300 | MPa | ISO 178 |
| Flexural Strength | |||
| 3.20 mm, Injection Molded | 80.7 | MPa | ASTM D790 |
| -- | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | ||
| -30°C | 30.0 | kJ/m² | |
| 23°C | 45.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 8 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| -29°C, 3.20 mm, Injection Molded | 530 | J/m | ASTM D256 |
| 23°C, 3.20 mm, Injection Molded | 640 | J/m | ASTM D256 |
| -40°C | 24 | kJ/m² | ISO 180 |
| -30°C | 32 | kJ/m² | ISO 180 |
| 23°C | 52 | kJ/m² | ISO 180 |
| Instrumented Dart Impact 9 | ASTM D3763 | ||
| -29°C, 3.20 mm, Peak Energy | 62.1 | J | |
| 23°C, 3.20 mm, Peak Energy | 56.5 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 129 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 128 | °C | ISO 75-2/B |
| 0.45 MPa | 126 | °C | ISO 75-2 10 |
| 1.8 MPa, Unannealed, 3.20 mm | 107 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 106 | °C | ISO 75-2/A |
| 1.8 MPa | 104 | °C | ISO 75-2 11 |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525 12 |
| -- | 142 | °C | ISO 306/A120 |
| -- | 128 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 128 | °C | ISO 306 13 |
| CLTE - Flow | |||
| -40 to 82°C | 7.4E-5 | cm/cm/°C | ASTM D696 |
| -- | 7.5E-5 | cm/cm/°C | ISO 11359-2 14 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°, Smooth) | 25 | ASTM D542 | |
| GMCP88 - Light Stipple | 6.5 | % | ASTM D542 |
| Monticello | 3.3 | % | ASTM D542 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | 6.60 m/sec |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Rate A (50°C/h), Loading 2 (50 N) |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-91-T3056D-75 | Teknor Apex Company | TPE | Telcar® |
| Stirol UPS-1002 L | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| NEXT REPROCESSED PA6 8267-300R | NEXT Specialty Resins, Inc. | Nylon 6 | NEXT REPROCESSED |
| ExxonMobil™ LDPE LD 250 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Lustran® 248BS | INEOS Styrolution Group GmbH | ABS | Lustran® |