Petrothene® NA940000 (Blow Molding)
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SabIvZ_Petrothene-NA940000-Blow-Molding-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA940000 is a low density homopolymer resin selected by customers for use in blow molding applications. Excellent toughness, good clarity and processibility are key attributes of NA940000. Typical customer applications include flexible containers, squeeze bottles and toys. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 14.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 600 | % | ASTM D638 |
| Flexural Modulus | 234 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 42.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 2100M | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Nycal™ 1820RMC40H Bk-1 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Dartek B-601 | DuPont Canada, Inc. - Dartek Division | Nylon 66 | Dartek |
| Hy-Vin® VQ130 | INEOS Compounds | PVC, Rigid | Hy-Vin® |
| O'Tech OF 6532 | O'Tech Corporation | PVC, Unspecified | O'Tech |