Resilience™ HC 8220
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Resilience™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SaUcTI_Resilience-HC-8220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resilience HC 8220 is a high flow, very high impact resistance rigid grade offering enhanced chemical resistance for medical device housing applications. It is RoHS compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Spiral Flow | 86.4 | cm | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2690 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 22 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| -18°C, 3.18 mm, Injection Molded | 110 | J/m | |
| 0°C, 3.18 mm, Injection Molded | 690 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 1100 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 68.9 | °C | |
| 0.45 MPa, Annealed, 3.18 mm | 72.8 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 68.9 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 72.8 | °C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ AT602 | Asahi Kasei Chemicals Corporation | Nylon+PPE | XYRON™ |
| GERMADUR HSZ | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| ESPRENE EPDM 600F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| LNP鈩?THERMOCOMP鈩?OF008G compound | SABIC Innovative Plastics | PPS, Linear | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ DF0029ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |