POLYFORT® FPP 1006
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | A. Schulman Inc. |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SaL18I_POLYFORT-FPP-1006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20% Talc |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 20 | % | ASTM D5630 |
| Note Message | |
|---|---|
| 1 . | 5x7 in plaque |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premi-Ject® 6100-20 | Premix, Inc. | TS, Unspecified | Premi-Ject® |
| STAR-THERM® E A-4C | EPIC Polymers | Nylon 66 | STAR-THERM® |
| Clariant Nylon 6/12 612G13-L | Clariant Corporation | Nylon 612 | Clariant Nylon 6/12 |
| IDI SMC S51 (Glass Content 25%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Karina CLEAR PVC COMPOUND 803-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |