Elastollan® C70AW
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SaGRgm_Elastollan-C70AW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® C70AW is a polyester-based thermoplastic polyurethane (TPU) containing a plasticizer. It exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C70AW is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/3.8 kg) | 10 to 30 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 11.0 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 13.1 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 40.0 | mg | ASTM D1044 |
| Abrasion - DIN | 20 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 89 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 4.14 | MPa | |
| 300% Strain | 10.3 | MPa | |
| Tensile Strength | 27.6 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 720 | % | ASTM D412 |
| Tear Strength 1 | 77.1 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -48.0 | °C | Internal Method |
| Vicat Softening Temperature | 67.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 to 175 | °C | |
| Cylinder Zone 3 Temp. | 140 to 175 | °C | |
| Cylinder Zone 5 Temp. | 140 to 175 | °C | |
| Adapter Temperature | 160 to 175 | °C | |
| Die Temperature | 165 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starpylen HZ 30WF2 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Moplen HP748H | HMC Polymers | PP Homopolymer | Moplen |
| NEXUS PP CPP2.5NB | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |
| Arak LLDPE LL0209AA / LL0209KJ | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Durez® 34163 | SBHPP | Phenolic | Durez® |