BCC Resins BC 5010
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SZrEMg_BCC-Resins-BC-5010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BC 5010 is a high quality, low viscosity room temperature curing laminating resin. A Safety System for the production of a variety if dimensionally stable fiberglass tools. BC 5010 features low odor and rapid "wet-out" with no vertical drain off. An excellent general purpose laminating resin to meet the tooling requirements for automotive, aircraft, and foundry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Ultimate) | 173 | MPa | ASTM D638 |
| Flexural Modulus | 13000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 210 | MPa | ASTM D790 |
| Compressive Strength | 266 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 87.8 | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 1.0, Mix Ratio by Volume: 1.0 | ||
| Resin | Mix Ratio by Weight: 6.0, Mix Ratio by Volume: 4.5 | ||
| Pot Life (25°C) | 25 to 30 | min | |
| Thermoset Mix Viscosity | 3200 | cP | ASTM D2393 |
| Demold Time (24°C) | 720 to 960 | min | |
| Post Cure Time (25°C) | 8.0 to 12 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0210 | Borealis AG | Plastomer | Queo™ |
| Shandong Aobang TPU-Polyester 95-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| VENYL SG300 - 8317 | AD majoris | Nylon 6 | VENYL |
| Sumiliteresin® PR-2243 I | SBHPP | Phenolic | Sumiliteresin® |
| POCAN® B 1100 000000 | LANXESS GmbH | PBT | POCAN® |