Westlake EF608 is a high melt index LDPE resin suggested for thin guage garment films and other films requiring excellent drawdown. The high melt index makes this material a good choice in compounding applications as a carrier for masterbatch or other concentrates. Application/Uses: Compounding base resin Color concentrates Additives masterbatches |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 51 µm, blown film | 152 | MPa | ASTM D882 |
| 1% secant, TD : 51 µm, blown film | 179 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 21.4 | MPa | ASTM D882 |
| TD : Broken, 51 µm, blown film | 15.9 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 51 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 51 µm, blown film | 730 | % | ASTM D882 |
| Dart Drop Impact 4(51 µm, Blown Film) | 95 | g | ASTM D1709 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 2.0 mils; blow up ratio 2.5:1, die gap 35 mils.Melt temperatures of 360° F - 400° F are recommended for Westlake Chemical EF608 with blow-up ratios of 1.5:1 or higher. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AECN Noir 03 TL | Arkema | Nylon 12 | Rilsamid® |
| Sylvin 9077-60 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Alkathene® XLF175 | Qenos Pty Ltd | LLDPE | Alkathene® |
| Geon™ Vinyl Rigid Extrusion 87560 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| POLYfill PPH B8075 | Polykemi AB | PP Homopolymer | POLYfill |