| 20 % Talc Filled CoPolymer PP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 22 | % | ASTM D638 |
| Flexural Modulus | 1640 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 33.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 880 | J/m | ASTM D256 |
| Gardner Impact | 23.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 117 | °C | |
| 1.8 MPa, Unannealed | 62.2 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 2.0E-3 | % | |
| Rear Temperature | 188 to 216 | °C | |
| Middle Temperature | 199 to 232 | °C | |
| Front Temperature | 199 to 232 | °C | |
| Nozzle Temperature | 193 to 227 | °C | |
| Processing (Melt) Temp | 204 to 260 | °C | |
| Mold Temperature | 18.3 to 54.4 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene FRP256-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Elastron® D D100.A72.B | Elastron USA, Inc. | SBS | Elastron® D |
| EPIGUM DPE/73 | Crosspolimeri S.p.A. | TPV | EPIGUM |
| Latamid 66 H2 G/60 | LATI S.p.A. | Nylon 66 | Latamid |
| LONOY lonoy 1600 | Kingfa | PC+PBT | LONOY |