FRblend® PBT-1303
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SWqIM7_FRblend-PBT-1303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PBT-1303 is an unfilled, flame retardant polybtylene-terephathalate compound. The flame retardant system is base on brominated aromatic flame retardant. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.8 to 2.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3870 | MPa | ASTM D638 |
| Tensile Strength | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 2970 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 160 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 71.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 235 to 245 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 to 260 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LXR518E | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Texalan® 5 Series 564D | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 5 Series |
| Expandable PS F32MB-n | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Guang Sung PVC GPMA70T | Guang Sung Plastics (GSPL) | PVC, Unspecified | Guang Sung PVC |
| HIDEN® F500 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |