Order Products : sales@su-jiao.com
LIHAN® A706SH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SW3yZY_LIHAN-A706SH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Glass fiber reinforced PA66 with hydrolyzing resistance Pamphlet: The special material has good mechanical properties and the flexural strength reaches 100MPa even after eroding at 135°C in 100% glycol solution for 48 hours. The material accords with the standard of the automobile water tank and can be used to produce automobile water tank and its accessory. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.60 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress (Break) | 180 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | -- | % | ISO 527-2 |
| Flexural Modulus | 9000 | -- | MPa | ISO 178 |
| Flexural Stress | ISO 178 | |||
| -- 1 | 105 | -- | MPa | |
| -- | 250 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 12 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | DSC |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | ASTM D257 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 100% Glycol Solution, 135°C, 48 Hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIPRO F2011 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Moplen HP563S | PolyMirae | PP Homopolymer | Moplen |
| Vipel® F007-AAA-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| Ferro PP LPP40YR01GY | Ferro Corporation | PP Copolymer | Ferro PP |
| LNP™ LUBRICOMP™ MG004 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ LUBRICOMP™ |