Grivory® HB 5299 HV
| Category: | Nylon MXD6/MXDI , Polyamide MXD6/MXDI Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grivory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SVvnSG_Grivory-HB-5299-HV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grivory® HB 5299 HV is a Polyamide MXD6/MXDI Copolymer (Nylon MXD6/MXDI) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for blow molding, blown film, cast film, or injection stretch blow molding. Primary attribute of Grivory® HB 5299 HV: High Viscosity. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.21 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 30.0 | -- | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4000 | -- | MPa | ISO 527-2 |
| Films | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-3 | |||
| MD : Break, 50 µm | 110 | -- | MPa | |
| TD : Break, 50 µm | 100 | -- | MPa | |
| Tensile Elongation | ISO 527-3 | |||
| MD : Break, 50 µm | 4.5 | -- | % | |
| TD : Break, 50 µm | 3.5 | -- | % | |
| Elmendorf Tear Strength | ISO 6383-2 | |||
| MD : 50 µm | 5.0 | -- | N | |
| TD : 50 µm | 5.0 | -- | N | |
| Water Vapor Transmission Rate (23°C, 85% RH, 50 µm) | 6.0 | -- | g/m²/24 hr | DIS 15106-1/-2 |
| Oxygen Permeability | DIS 15105-1/-2 | |||
| 23°C, 50.0 µm 1 | 4.0 | -- | cm³/m²/bar/24 hr | |
| 23°C, 50.0 µm 2 | 4.0 | -- | cm³/m²/bar/24 hr | |
| Carbon Dioxide Transmission Rate | DIS 15105-1/-2 | |||
| 23°C, 50.0 µm 3 | 15.0 | -- | cm³/m²/bar/24 hr | |
| 23°C, 50.0 µm 4 | 15.0 | -- | cm³/m²/bar/24 hr |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA MXD6/MXDI, FNST, 12-040 | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 5 | 218 | -- | °C | ISO 11357-3 |
| Optical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Gloss (60°, 50.0 µm) | 150 | -- | ISO 2813 |
| Note Message | |
|---|---|
| 1 . | 85% RH |
| 2 . | 0% RH |
| 3 . | 0% RH |
| 4 . | 85% RH |
| 5 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer P-11030-GF | Polylink Polymers (India) Ltd. | TPO | Polylink Polymer |
| Shuang-Bang AB-120OKA | Shuang-Bang Industrial Corp. | PUR, Unspecified | Shuang-Bang |
| FHR Polypropylene 13T10Acs279 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Keltan® 8570C | LANXESS Buna GmbH | EPDM | Keltan® |
| Durethan® C 38 FAM 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |