| Standard viscosity polyamide 66, 30% glass beads reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 0.85 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 6.3 | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4800 | MPa | ASTM D638 |
| Tensile Strength (Break) | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638 |
| Flexural Modulus | 4200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 425 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 285 | °C | |
| Front Temperature | 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E585PKOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| FHR Polypropylene 21N2A | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Hyundai EP Breathable AT880H/2102 | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Breathable |
| Mablex PCA | Ravago Group | PC+ABS | Mablex |
| PENTAMID A GK30 H schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |