Clariant Nylon 6 R60G33-L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | STSLxZ_Clariant-Nylon-6-R60G33-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clariant Nylon 6 R60G33-L is a Polyamide 6 (Nylon 6) material filled with 33% glass fiber. It is available in North America. Primary attribute of Clariant Nylon 6 R60G33-L: Lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Tensile Impact Strength | 11.3 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 | °C | |
| 1.8 MPa, Unannealed | 191 | °C | |
| Melting Temperature | 216 to 221 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ G90A-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |
| CERTENE™ LLBF-120F | Muehlstein | LLDPE | CERTENE™ |
| FHR Polypropylene P4C5B-030 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Karina GRAY PVC COMPOUND 702-DA-18/406-BZ-AS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF008XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |