Edgetek™ PA-60GF/000 BK006
| Category: | HPPA , High Performance Polyamide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | STLcwK_Edgetek-PA-60GF-000-BK006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber Reinforced PPA Compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.10 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 230 | MPa | ISO 527-2 |
| Flexural Modulus | 19000 | MPa | ISO 178 |
| Flexural Strength | 390 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 290 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 320 - 340 | °C | |
| Middle Temperature | 320 - 340 | °C | |
| Front Temperature | 320 - 340 | °C | |
| Mold Temperature | 120 - 135 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-102 | Lubrizol Advanced Materials, Inc. | PE Alloy | Stat-Rite® |
| Torayca® 3101T-20V | Toray Resin Company | Nylon 66 | Torayca® |
| Karina IVORY PVC COMPOUND 837-35/1-E-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LTP CE-2212 | Chengdu Letian Plastics Co., Ltd | PPS | LTP |
| ESTOPLAST EP 4030WW23 | Ester Industries Ltd. | PBT | ESTOPLAST EP |