Vyncolit FS-10-V0-P is a diallyl phthalate (DAP) material, and its filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing methods are: resin transfer molding, compression molding or injection molding. The main features of the Vyncolit FS-10-V0-P are: flame retardant/rated flame chemical resistance Flame Retardant Good dimensional stability moisture resistance Typical application areas include: Electrical/electronic applications Wire and cable Aerospace military applications

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Good dimensional stability Moisture resistance Antibacterial property Solvent resistance Impact resistance, high Good electrical performance Good chemical resistance alkali resistance Good wear resistance Fuel resistance Heat resistance, high acid resistance Flame retardancy
Uses	Membrane key switch Aircraft applications Insulating material Connector Communication Equipment
Agency Ratings	MIL C-24308
Forms	Particles
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.91	g/cm³	ASTM D792
Bulk Factor	2.3		ASTM D1895
Molding Shrinkage - Flow (Compression Molded)	0.20 - 0.40	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	75.8	MPa	ASTM D638
Flexural Modulus	11700	MPa	ASTM D790
Flexural Strength	131	MPa	ASTM D790
Compressive Strength	152	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	32	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	260	°C	ASTM D648
CLTE - Flow	1.8E-5	cm/cm/°C	ASTM D696
Thermal Conductivity	0.36	W/m/K	ASTM C177
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	15	kV/mm	ASTM D149
-- ²	14	kV/mm	ASTM D149
Dielectric Constant			ASTM D150
1 kHz	4.10		ASTM D150
1 MHz	3.90		ASTM D150
Dissipation Factor			ASTM D150
1 kHz	0.011		ASTM D150
1 MHz	0.016		ASTM D150
Arc Resistance	175	sec	ASTM D495
Comparative Tracking Index (CTI)	600	V	UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.59 mm	V-0		UL 94
3.18 mm	V-0		UL 94
Oxygen Index	50	%	ASTM D2863

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	76.7	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	110 - 116	°C
Mold Temperature	160 - 182	°C

Injection instructions
Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Resin Isomer, DAP: ISOWater Absorption, ASTM D570, 48 hrs, 50°C: 0.35%Flammability Ignition, ASTM D229: 130 secFlammability Burn, ASTM D229: 50 secDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 375 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 350 V/milDielectric Constant, ASTM D150, 1000 Hz, wet: 4.1Dielectric Constant, ASTM D150, 1000000 Hz, wet: 3.9Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.011Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.016Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Injection instructions

Plastication: 50rpmBack Pressure (gauge): slightInjection Pressure: set to give 5 to 15 sec injection timeHold Pressure: 1/2 of injection pressureCure Time, 0.125 in: 40 secThe value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM F433.Resin Isomer, DAP: ISOWater Absorption, ASTM D570, 48 hrs, 50°C: 0.35%Flammability Ignition, ASTM D229: 130 secFlammability Burn, ASTM D229: 50 secDielectric Strength, ASTM D149, 60 Hz, Method A, wet: 375 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 350 V/milDielectric Constant, ASTM D150, 1000 Hz, wet: 4.1Dielectric Constant, ASTM D150, 1000000 Hz, wet: 3.9Dissipation Factor, ASTM D150, 1000 Hz, wet: 0.011Dissipation Factor, ASTM D150, 1000000 Hz, wet: 0.016Compression and Transfer Molding Conditions: Preforming Pressure: 8000 to 12000 psi Preheat Temperature: 220 to 230 °F Preheat Time: 45 sec Mold Temperature: 320 to 350 °F Compression Mold Pressure: 3500 to 6000 psi Transfer Mold Pressure: 2500 to 5000 psi Cure Time, 0.125 in: 45 to 70 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	DAP , Diallyl Phthalate
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	SSnLaT_Vyncolit-FS-10-V0-P.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Durethan® BKV 60 H2.0 EF DUS060 900116	LANXESS GmbH	Nylon 6	Durethan®
Duroloy® AS-61	Unigel Plásticos	PC+ABS	Duroloy®
HIVOREX 5305E	Lotte Chemical Corporation	HDPE	HIVOREX
IDI SMC S30 (Glass Content 20%)	IDI Composites International	TS, Unspecified	IDI SMC
LUVOCOM® 1-7139-1	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®