Kepex® 3300M
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SSNag5_Kepex3300M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| shrinkage- Flow (3.00 mm) | 2.1 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 63.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 15 | % | ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ISO 178 |
| Flexural Stress | 94.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.9 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 68.0 | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant (60 Hz) | 3.00 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Hopper Temperature | 60 - 80 | °C | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 70 - 90 | °C | |
| Back Pressure | 0.490 - 0.981 | MPa | |
| Screw Speed | 80 - 120 | rpm |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ShinkoLite-P IR H-50 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| SUSTARIN® H AF | Röchling Sustaplast SE & Co. KG | Acetal (POM) Homopolymer | SUSTARIN® |
| AKROMID® A3 GF 15 1 L black (4673) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Axiall PVC 1901 Clear 7002 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| HONES® PA66 G25 | Guangdong Shunde Hones Polymer Material Co., Ltd. | Nylon 66 | HONES® |