NORYL™ EZ250 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SSNO1m_NORYL-EZ250-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Automotive wheel covers. Offers superior processability/flow and better chemical resistance when exposed to many automotive fluids over PX0844. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 2000 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 68.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 130 | J/m | |
| 23°C | 290 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 33.9 | J | |
| 23°C, Energy at Peak Load | 39.5 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 127 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 113 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 243 to 293 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Nozzle Temperature | 277 to 304 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 600 FR UV | RTP Company | ABS | RTP |
| Prixene® PH350I04 | POLYMAT | PP Homopolymer | Prixene® |
| Argothane® 49510 | Argotec LLC | TPU, Unspecified | Argothane® |
| KumhoSunny PC/AES HEC0255B | Shanghai KumhoSunny Plastics Co., Ltd. | AES+PC | KumhoSunny PC/AES |
| LNP™ THERMOCOMP™ RX06420 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |