TAROLOX 111 G7
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SPRwch_TAROLOX-111-G7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PET glass fiber reinforced 35%, very high temperature resistance, very good chemical resistance, very good mechanical, thermal and electrical properties, very low moisture absorption, very good dimensional stability. Product must be dryed before moulding. Available: all colors, heat stabilized (H), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 to 1.64 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.15 to 0.30 | % | |
| Across Flow | 0.40 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570, ISO 62 |
| Granule Humidity | < 0.030 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 145 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 245 | MPa | ISO 178 |
| Break | 245 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 10 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 50 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 225 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50, ASTM D1525 3 |
| Ball Pressure Test (245°C) | Pass | USI 182-2 | |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 34 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 90.0 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CYCOLOY™ C7210A resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |
| CYCOLAC™ MG47 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| EVALENE® PP PHJ1201 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| ENVIROSUN® ENV31-NC730 | ENVIROPLAS®, Inc. | ASA | ENVIROSUN® |
| LubriOne™ LB3300-5002 RS BK | PolyOne Corporation | PBT | LubriOne™ |