Vyncolit® TX10916/30/1
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SP9K3C_VyncolitTX10916301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® TX10916/30/1 is a graphite filled phenolic molding compound used for low friction applications where dimensional stability is required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Apparent Density | 0.86 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.54 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.030 | % | ISO 62 |
| Post Shrinkage | 0.11 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.68 | % | ISO 178 |
| Tensile Modulus | 16000 | MPa | ISO 527-2 |
| Tensile Stress | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.39 | % | ISO 527-2 |
| Flexural Modulus | 13000 | MPa | ISO 178 |
| Flexural Stress | 83.0 | MPa | ISO 178 |
| Compressive Stress | 161 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.3 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 3.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 159 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 2.0E-5 | cm/cm/°C | TMA |
| Lateral | 3.1E-5 | cm/cm/°C | TMA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT HV1006S | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| Starglas FX05032 | Eurostar Engineering Plastics | PE, Unspecified | Starglas |
| AME™ 5001 resins | Ashland Performance Materials | Vinyl Ester | AME™ |
| HIVOREX J2200 | Lotte Chemical Corporation | HDPE | HIVOREX |
| Karina GRAY PVC COMPOUND 822-18/599-CRB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |