DynaStat® 157
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaStat® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SOwFDN_DynaStat-157.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Antistatic Polypropylene Compound Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 - 0.960 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 13.8 | MPa | ASTM D638 |
| Fracture | 51.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 24 | % | ASTM D638 |
| Fracture | > 500 | % | ASTM D638 |
| Flexural Modulus | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | No Break | ASTM D256 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 - 1.0E+8 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+6 - 8.0E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 188 - 196 | °C | |
| Middle Temperature | 196 - 204 | °C | |
| Front Temperature | 199 - 210 | °C | |
| Nozzle Temperature | 202 - 213 | °C | |
| Processing (Melt) Temp | 210 - 216 | °C | |
| Mold Temperature | 26.7 - 60.0 | °C | |
| Injection Pressure | 34.5 - 55.2 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 399 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 188 - 196 | °C | |
| Cylinder Zone 3 Temp. | 193 - 202 | °C | |
| Cylinder Zone 5 Temp. | 199 - 210 | °C | |
| Melt Temperature | 204 - 216 | °C | |
| Die Temperature | 199 - 216 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 25 to 100 Rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirathane™ E695 | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| VALOX™ HX3091HP resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Badadur® PBT8 FR HF | Bada AG | PBT | Badadur® |
| Gallonprene® GP640-9001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LNP™ THERMOCOMP™ WX93111 compound | SABIC Innovative Plastics Europe | PBT | LNP™ THERMOCOMP™ |