TRANSMARE® 35HNF30-0.101
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SNsdMU_TRANSMARE-35HNF30-0-101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 35HNF30-0.101 is a 30% BF-K100 bamboo fiber reinforced polypropylene homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 9.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 3050 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00mm | 27.0 | MPa | ISO 527-2/50 |
| Fracture, 4.00mm | 36.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00mm | 2.5 | % | ISO 527-2/50 |
| Fracture, 4.00mm | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus | 2850 | MPa | ISO 178 |
| Flexural Stress | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 1.1 | kJ/m² | ISO 179/1A |
| 23°C | 2.1 | kJ/m² | ISO 179/1A |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 7.7 | kJ/m² | ISO 179/1U |
| 23°C | 11 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 160 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 | °C | |
| Middle Temperature | 160 | °C | |
| Front Temperature | 175 | °C | |
| Nozzle Temperature | 180 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| In specific cases pre-drying of this material might be required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Power Cable PP 408/401 | Polylink Polymers (India) Ltd. | XLPE | Polylink Power Cable |
| AKROLOY® PA GF 60 8 black (4174) | AKRO-PLASTIC GmbH | Nylon 66+Nylon 6I/6T | AKROLOY® |
| Estane® AG 8451 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Petlon Prime A1-G50-00-BK | Petlon Polymers Ltd | Nylon 66 | Petlon Prime |
| Plaslube® PA6/6,6 GF50 HS L | Techmer Engineered Solutions | Nylon 66/6 | Plaslube® |