SAXAMID™ 226F7
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SNIQ7P_SAXAMID-226F7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 226F7 is a general purpose polyamide 6.6 injection-molding-grade reinforced with 35 % glass fibres. This grade has very high mechanical strength in combination with good impact resistance. This compound is characterized by high mechanical strength over a long period and is able to perform at higher temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 215 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 8500 | MPa | ISO 178 |
| Flexural Stress 2 | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 86 | kJ/m² | |
| 23°C | 96 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 80 | kJ/m² | |
| 23°C | 90 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 248 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPUI-E85 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| TUFNYL® SFM 24 DARK GREY | SRF Ltd. | Nylon 6 | TUFNYL® |
| Novamid® 1015C | DSM Engineering Plastics | Nylon 6 | Novamid® |
| Innoprene 1350N/B | Kumho Polychem Co., Ltd. | TPV | Innoprene |
| TOTAL Polypropylene PPR 12236 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |