G-PAEK™ 1230FCT
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | G-PAEK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SMbTk6_G-PAEK-1230FCT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high performance lubricated polymer, carbon fiber, PTFE, graphite, HBN and MoS 2 filled in Polyether Ketone, semi-crystalline granules suitable for injection molding, easy flow, Black in color. Application Areas: Suitable for high temperature applications, where higher strength & stiffness in load- bearing applications is required. Excellent wear resistance. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | |
| Molding Shrinkage 1 | |||
| Flow | 0.10 | % | |
| Across Flow | 0.42 | % | |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 106 | ASTM D785 | |
| Durometer Hardness (Shore D) | 91 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 19000 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.2 | % | ASTM D638 |
| Flexural Modulus (23°C) | 17500 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 210 | MPa | ASTM D790 |
| Coefficient of Friction | 0.10 | ||
| Wear Factor | 2.7E-5 | 10^-8 mm³/N·m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 45 | J/m | ASTM D256 |
| Unnotched Izod Impact | 510 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 348 | °C | ASTM D648 |
| Continuous Use Temperature | 280 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 420 | °C | |
| Processing (Melt) Temp | 390 to 420 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 410°C nozzle, 220°C Mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1322 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Ryton® QA200P | Solvay Specialty Polymers | PPS | Ryton® |
| Sanren Q200 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| AKROMID® B3 GF 45 1 natural (3983) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| ISOTHANE® 1085AF | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |