SABIC® PPcompound 9135
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SMG9w5_SABIC-PPcompound-9135.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 9135 is an elastomer-modified mineral filled Polypropylene with excellent impact and stiffness ratio. Typical material application are esthetical automotive interior parts. It has a very high scratch resistance, no stickiness and a high flow. SABIC® PPcompound 9135 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 18.0 | MPa | |
| Break, Injection Molded | 12.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/4A | ||
| 0°C, Injection Molded | 7.0 | kJ/m² | |
| 23°C, Injection Molded | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 2608 | Covestro - Polycarbonates | PC | Makrolon® |
| Shin-Etsu RTV KE-1223 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-2 | Shin-Etsu RTV |
| Nipol® Roadace | Zeon Corporation | Latex | Nipol® |
| Grivory® HTV-4H1 nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| ROTOLENE® Industrial | Polimeros Mexicanos S.A. de C.V. | LMDPE | ROTOLENE® |